VESTAMID® L2106F nc (nf)|PA12|Evonik Industries物性表报告及物性特性介绍,VESTAMID® L2106F nc (nf)|PA12|Evonik Industries注塑参数详情-塑料物性表查询网

Product TextsVESTAMID® L2106F nc EG-Standard 90/128.7 / *	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	1.2 / *	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	1300 / 1100	MPa	ISO 527-1/-2
屈服应力(Yield stress)	45 / 36	MPa	ISO 527-1/-2
屈服应变(Yield strain)	5 / 11	%	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	>50 / >50	%	ISO 527-1/-2
Tensile creep modulus (1h)	* / 800	MPa	ISO 899-1
Tensile creep modulus (1000h)	* / 450	MPa	ISO 899-1
简支梁冲击强度(Charpy impact strength) (+23°C)	N / N	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	N / N	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	7 / 12	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	7 / 10	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	175 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	40 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	80 / *	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	130 / *	°C	ISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	150 / *	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	150 / *	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6 / *	mm	IEC 60695-11-10
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	3.2 / *	mm	IEC 60695-11-10

电气性能(Electrical properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (100Hz)	3.7 / 5.5	-	IEC 60250
相对介电常数(Relative permittivity) (1MHz)	3 / 3.1	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (100Hz)	450 / 1000	E-4	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	280 / 600	E-4	IEC 60250
体积电阻率(Volume resistivity)	>1E13 / 1E12	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	* / >1E15	Ohm	IEC 60093
电气强度(Electric strength)	27 / 30	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	600 / 600	-	IEC 60112

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	1.8 / *	%	Sim. to ISO 62
吸湿性(Humidity absorption)	0.8 / *	%	Sim. to ISO 62
密度(Density)	1010 / 1010	kg/m³	ISO 1183

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	230	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724
Injection Molding, injection velocity	200	mm/s	ISO 294
Injection Molding, pressure at hold	70	MPa	ISO 294

CharacteristicsProcessingInjection Molding, Film Extrusion, Other ExtrusionDelivery formPelletsRegional AvailabilityNorth America, Europe, Asia Pacific, South and Central America, Near East/AfricaOther text informationInjection moldingPREPROCESSING INFORMATION1 % The drying time is dependentAt a drying temperature of 80°C we recommend, depending on the waterFresh air dryers are acceptable, better would be a dry air orPlease note our product literature, plasticized resins can lose plasticizer during 1 % The drying time is dependentAt a drying temperature of 80°C we recommend, depending on the water Fresh air dryers are acceptable, better would be a dry air orPlease note our product literature, plasticized resins can lose plasticizer dur1 % The drying time is dependentAt a drying temperature of 80°C we recommend, depending on the waterFresh air dryers are acceptable, better would be a dry air orPlease note our product literature, plasticized resins can lose plasticizer du .