Pearlthane® 11T92E|TPU|Merquinsa物性表报告及物性特性介绍,Pearlthane® 11T92E|TPU|Merquinsa注塑参数详情-塑料物性表查询网

Product TextsPEARLTHANE® 11T92E can be extruded into profiles, belts, tubes and film. In the case of injection molding, this grade is only recommended for certain specific applications, e.g. when large, hard-to-fill mould cavities are used.

加工/物理特性	值(Value)	单位(Unit)	测试标准(Test Standard)
ASTM数据(ASTM Data)
密度(Density) (73°F)	1170	kg/m³	ASTM D 792

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
Stress at 100% elongation	10	MPa	ISO 527-1/-2
Stress at 300% elongation	63	MPa	ISO 527-1/-2
破坏时应变(Strain at break) TPE	>300	%	ISO 527-1/-2
破坏时应变(Stress at break) TPE	42	MPa	ISO 527-1/-2
压缩设置下的恒应变(Compression Set under constant strain) (23°C)	25	%	ISO 815
压缩设置下的恒应变(Compression Set under constant strain) (70°C)	45	%	ISO 815
Abrasion resistance	25	mm³	ISO 4649
邵尔A硬度(Shore A hardness) (3s)	93	-	ISO 868
ASTM数据(ASTM Data)
抗拉强度(Tensile Strength) at Break	42	MPa	ASTM D 638
断裂伸长率(Elongation at Break)	560	%	ASTM D 638
Modulus at 100% Elongation	10	MPa	ASTM D 412
Modulus at 300% Elongation	21	MPa	ASTM D 412
Shore A Hardness	93	-	ASTM D 2240
撕裂强度(Tear Strength)	130	kN/m	ASTM D 624

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
玻璃化转变温度(Glass transition temperature) (10°C/min)	-34	°C	ISO 11357-1/-2

CharacteristicsProcessingInjection Molding, Film Extrusion, Other ExtrusionDelivery formPelletsRegional AvailabilityNorth America, EuropeDisclaimerCopyright M-Base .