Pearlcoat® 165K|TPU|Merquinsa物性表报告及物性特性介绍,Pearlcoat® 165K|TPU|Merquinsa注塑参数详情-塑料物性表查询网

Product TextsPEARLCOAT® D165K is used in melt coatings on textile substrates, for end-uses in industrial coatings (for life-jackets, etc.) obtained by extrusion and calendering.

加工/物理特性	值(Value)	单位(Unit)	测试标准(Test Standard)
ASTM数据(ASTM Data)
密度(Density) (73°F)	1120	kg/m³	ASTM D 792

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
Stress at 100% elongation	7	MPa	ISO 527-1/-2
Stress at 300% elongation	36	MPa	ISO 527-1/-2
破坏时应变(Strain at break) TPE	>300	%	ISO 527-1/-2
破坏时应变(Stress at break) TPE	30	MPa	ISO 527-1/-2
压缩设置下的恒应变(Compression Set under constant strain) (23°C)	25	%	ISO 815
压缩设置下的恒应变(Compression Set under constant strain) (70°C)	35	%	ISO 815
Abrasion resistance	25	mm³	ISO 4649
邵尔A硬度(Shore A hardness) (3s)	90	-	ISO 868
ASTM数据(ASTM Data)
抗拉强度(Tensile Strength) at Break	30.1	MPa	ASTM D 638
断裂伸长率(Elongation at Break)	450	%	ASTM D 638
Modulus at 100% Elongation	7.01	MPa	ASTM D 412
Modulus at 300% Elongation	12	MPa	ASTM D 412
Shore A Hardness	90	-	ASTM D 2240
Compression Set(22 hr @ 158 °F)	35	%	ASTM D 395

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
熔化温度(熔化温度(Melting temperature)) (10°C/min)	167	°C	ISO 11357-1/-3
玻璃化转变温度(Glass transition temperature) (10°C/min)	-43	°C	ISO 11357-1/-2

CharacteristicsProcessingFilm Extrusion, CoatingDelivery formPelletsChemical ResistanceHydrolytically StableEcological valuationFood approval FDA 21 CFRRegional AvailabilityNorth America, EuropeDisclaimerCopyright M-Base .