Product TextsThe data for this material was provided by Plastinfo.ru.流变性能(Rheological properties) | 值(Value) | 单位(Unit) | 测试标准(Test Standard) | ISO数据 | 熔体流动指数(熔体流动指数(Melt flow index)) (MFI) | 2 | g/10min | ISO 1133 | MFI温度(MFI temperature) | 190 | °C | ISO 1133 | MFI负载(MFI load) | 2.16 | kg | ISO 1133 |
机械性能(机械性能(Mechanical properties)) | 值(Value) | 单位(Unit) | 测试标准(Test Standard) | ISO数据 | 拉伸模量(Tensile Modulus) | 280 | MPa | ISO 527-1/-2 | 断裂拉伸应变(Nominal strain at break) | >50 | % | ISO 527-1/-2 | 破坏时应变(Stress at break) | 12.2 | MPa | ISO 527-1/-2 | 破坏时应变(Strain at break) | >50 | % | ISO 527-1/-2 | 弯曲弹性模量(Flexural modulus) (23°C) | 98 | MPa | ISO 178 |
热性能(热性能(Thermal properties)) | 值(Value) | 单位(Unit) | 测试标准(Test Standard) | ISO数据 | 熔化温度(熔化温度(Melting temperature)) (10°C/min) | 110 | °C | ISO 11357-1/-3 | Vicat softening temperature A | 100 | °C | ISO 306 | COEFF线性热(Coeff. of linear therm. expansion) (parallel) | 550 | E-6/K | ISO 11359-1/-2 |
电气性能(Electrical properties) | 值(Value) | 单位(Unit) | 测试标准(Test Standard) | ISO数据 | 相对介电常数(Relative permittivity) (1MHz) | 2.2 | - | IEC 60250 | 耗散因数(耗散因数(Dissipation factor)) (1MHz) | 0.0002 | E-4 | IEC 60250 | 体积电阻率(Volume resistivity) | >1E13 | Ohm*m | IEC 60093 | 表面电阻率(Surface resistivity) | 1E15 | Ohm | IEC 60093 | 电气强度(Electric strength) | 40 | kV/mm | IEC 60243-1 |
其他属性(Other properties) | 值(Value) | 单位(Unit) | 测试标准(Test Standard) | ISO数据 | 吸水率(Water absorption) | 0.02 | % | Sim. to ISO 62 | 密度(Density) | 919 | kg/m³ | ISO 1183 |
材料特殊性能(Material specific properties) | 值(Value) | 单位(Unit) | 测试标准(Test Standard) | ISO数据 | 粘数(Viscosity number) | 1.5 | cm³/g | ISO 307, 1157, 1628 | CharacteristicsProcessingInjection Molding, Film Extrusion, Profile Extrusion, Sheet Extrusion, Other Extrusion, Coating, Blow Molding, Transfer Molding, Thermoforming, Bead Foam Molding, Compression Molding, Rotational Molding, Blown Film Extrusion, Fiber Extrusion, Pipe/Tube Extrusion, Laser SinteringDelivery formNatural ColorAdditivesBlowing agent, Antiblocking agentSpecial CharacteristicsTransparentFeaturesAcoustical Barrier Properties, Crosslinkable, Ductile, Foamable, Heat Sealable, Low Odor, HomopolymerChemical ResistanceAcid Resistance, Alkali Resistance, General Chemical Resistance, Environmental Stress Crack Resistance, Solvent ResistanceApplicationsAutomotive, Building Construction, Chemical Process, Electrical and Electronical, General Purpose, Medical, Monofilament, Packaging, Slit Film, Sports EquipmentRegional AvailabilityEuropeDisclaimerCopyright M-Base .
|
|