Faradex NX96302|(PC+ABS)-MF(Fe)|SABIC_IP物性表报告及物性特性介绍,Faradex NX96302|(PC+ABS)-MF(Fe)|SABIC

加工/物理特性	值(Value)	单位(Unit)	测试标准(Test Standard)
ASTM数据(ASTM Data)
模具收缩(Mold Shrinkage) (MD)	0.004	mm/mm	ASTM D 955
模具收缩(Mold Shrinkage) (TD)	0.006	mm/mm	ASTM D 955
密度(Density) (73°F)	1320	kg/m³	ASTM D 792

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)	3450	MPa	ISO 527-1/-2
屈服应变(Yield strain)	3.2	%	ISO 527-1/-2
破坏时应变(Stress at break)	60	MPa	ISO 527-1/-2
弯曲弹性模量(Flexural modulus) (23°C)	3390	MPa	ISO 178
悬臂梁式冲击切口 (23°C)	6	kJ/m²	ISO 180/1A
悬臂梁式冲击无切口(Izod Impact unnotched) (23°C)	30	kJ/m²	ISO 180/1U
ASTM数据(ASTM Data)
拉伸模量(Tensile Modulus)	3300	MPa	ASTM D 638
抗拉强度(Tensile Strength) at Yield	62	MPa	ASTM D 638
抗拉强度(Tensile Strength) at Break	54	MPa	ASTM D 638
屈服伸长率(Elongation at Yield)	3.7	%	ASTM D 638
断裂伸长率(Elongation at Break)	6.1	%	ASTM D 638
弯曲弹性模量(弯曲弹性模量(Flexural Modulus))	3590	MPa	ASTM D 790
悬臂梁式冲击切口 (1/8 in)	0.0519	kJ/m	ASTM D 256

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	94	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	103	°C	ISO 75-1/-2
ASTM数据(ASTM Data)
热膨胀系数(Coefficient of Thermal Expansion) (MD)	61	E-6/K	ASTM D 696
热膨胀系数(Coefficient of Thermal Expansion) (TD)	67	E-6/K	ASTM D 696
DTUL @ 66 psi	103	°C	ASTM D 648
DTUL @ 264 psi	96	°C	ASTM D 648

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ASTM数据(ASTM Data)
表面电阻率(Surface Resistivity)	3	Ohm	ASTM D 257

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据
吸湿性(Humidity absorption)	0.17	%	Sim. to ISO 62

CharacteristicsProcessingInjection MoldingRegional AvailabilityNorth America, South and Central AmericaDisclaimerCopyright M-Base Engineering+Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from M-Base; this is especially valid for claims of compensation resulting from consequential damages. M-Base explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.