Technyl® A 216|PA66|Rhodia物性表报告及物性特性介绍,Technyl® A 216|PA66|Rhodia注塑参数详情-塑料物性表查询网

Product TextsUnreinforced polyamide 66, medium viscosity, for injection moulding. 2 / 30	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	N / N	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	4.5 / 14	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	263 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	75 / *	°C	ISO 75-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	70 / *	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	V-2 / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6 / *	mm	IEC 60695-11-10
UL 识别(recognition)	UL / *	-	-
燃烧性(球压痕硬度(Burning behav)). at thickness h	V-2 / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	0.8 / *	mm	IEC 60695-11-10
UL 识别(recognition)	UL / *	-	-
Oxygen index	26.5 / *	%	ISO 4589-1/-2

电气性能(Electrical properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (1MHz)	2.9 / 3.2	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	300 / 800	E-4	IEC 60250
体积电阻率(Volume resistivity)	>1E13 / 1E12	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	* / 1E13	Ohm	IEC 60093
电气强度(Electric strength)	30 / 26	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	600 / 575	-	IEC 60112

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	1.3 / *	%	Sim. to ISO 62
密度(Density)	1140 / -	kg/m³	ISO 1183

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	225	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724

Diagrams In the case that the virgin material has absorbed moisture, it must be dried to a final moisture content of less than 0,2% with a dehumidified air drying equipment at approx 80°C.ISO 1817 Liquid 4) (23°C)[/td][/tr][tr][td]Salt solutions[/td][/tr][tr][td] .
[/td][/tr][/table]