Ultramid® 1003-2 NF2002|PA66|BASF物性表报告及物性特性介绍,Ultramid® 1003-2 NF2002|PA66|BASF注塑参数详情-塑料物性表查询网

Product TextsUltramid® 1003-2 NF2002 is a general purpose, heat stabilized PA6/6.

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	3000 / 1250	MPa	ISO 527-1/-2
屈服应力(Yield stress)	85 / 54	MPa	ISO 527-1/-2
屈服应变(Yield strain)	5 / 25	%	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	25 / >50	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	N / N	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	N / N	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	5.7 / 13	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	4 / 4	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	257 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	72 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	205 / *	°C	ISO 75-1/-2

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	8.5 / *	%	Sim. to ISO 62
吸湿性(Humidity absorption)	2.5 / *	%	Sim. to ISO 62
密度(Density)	1140 / -	kg/m³	ISO 1183

Diagrams Polyamid 66 materials are hygroscopic and will become degraded by excessive moisture during the injection molding process. For unopened bag/box, dry at 140 F (60 °C). For material exposed to the atmosphere, if additional drying time is needed, dry at 150 F (66 °C) until the moisture level is between 0.04 and 0.20%. Do not overdry the resin. .