Ultramid® 1503-2 NF2004|PA66-GF33|BASF物性表报告及物性特性介绍,Ultramid® 1503-2 NF2004|PA66-GF33|BASF注塑参数详情-塑料物性表查询网

Product TextsUltramid® 1503-2 NF2004 is a 33% glass reinforced, heat stabilized injection molding PA6/6.

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	10800 / 7400	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	210 / 145	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	3 / 5	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	90 / 100	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	75 / 75	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	12 / 15	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	11 / 11	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	257 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	255 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	264 / *	°C	ISO 75-1/-2

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	5.7 / *	%	Sim. to ISO 62
吸湿性(Humidity absorption)	1.7 / *	%	Sim. to ISO 62
密度(Density)	1400 / -	kg/m³	ISO 1183

Diagrams PA66 materials are hygroscopic and will become degraded by excessive moisture during the injection molding process. For unopened bag/box, dry at 140F (60°C) for 1-2 hours. For material exposed to the atmosphere, if additional drying is needed, dry at 150F (66°C) or until the moisture level is between 0.04 - 0.20%.35 MPa (0 - 50 psi) Pac It should be applied and maintained until the gate area is completely frozen off.DisclaimerCopyright M-Base .