Product TextsGlass fibre reinforced injection moulding grade for machinery components and housings of high stiffness and dimensional stability such as lamp socket housings, cooling fans, insulating profile for aluminium window frames, water containers for automotive cooling systems, as well as electrically insulating parts.

加工/物理特性	值(Value)	单位(Unit)	测试标准(Test Standard)
ASTM数据(ASTM Data)
模具收缩(Mold Shrinkage) (MD)	0.003	mm/mm	ASTM D 955
密度(Density) (73°F)	1360	kg/m³	ASTM D 792
吸水率(Water Absorption) (Equilibrium)	5.5	%	ASTM D 570

流变性能(Rheological properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔体体积流动速率(Melt volume-flow rate) (MVR)	30 / *	cm³/10min	ISO 1133
温度(Temperature)	275 / *	°C	ISO 1133
负载(Load)	5 / *	kg	ISO 1133
成型收缩(Molding shrinkage) (parallel)	0.4 / *	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	1.1 / *	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	10000 / 7200	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	190 / 130	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	3 / 5	%	ISO 527-1/-2
Tensile creep modulus (1000h)	* / 5300	MPa	ISO 899-1
简支梁冲击强度(Charpy impact strength) (+23°C)	85 / 100	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	70 / -	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	13 / 22	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	11 / -	kJ/m²	ISO 179/1eA
ASTM数据(ASTM Data)
抗拉强度(Tensile Strength) at Break	186	MPa	ASTM D 638
断裂伸长率(Elongation at Break)	3	%	ASTM D 638
悬臂梁式冲击切口 (1/8 in)	0.112	kJ/m	ASTM D 256
悬臂梁式冲击切口 (Low-温度(Temperature))	0.091	kJ/m	ASTM D 256
温度(Temperature)	-40	°C	ASTM D 256

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	260 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	250 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	250 / *	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	250 / *	°C	ISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	25 / *	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	65 / *	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6 / *	mm	IEC 60695-11-10
UL 识别(recognition)	UL / *	-	-
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	0.8 / *	mm	IEC 60695-11-10
UL 识别(recognition)	UL / *	-	-
Oxygen index	24 / *	%	ISO 4589-1/-2
ASTM数据(ASTM Data)
UL 94 阻燃等级(Flame rating)	HB	-	UL 94
厚度测试(Thickness tested)	1.5	mm	-
DTUL @ 66 psi	250	°C	ASTM D 648
DTUL @ 264 psi	250	°C	ASTM D 648
熔化温度(Melting 温度(Temperature))	260	°C	ASTM D 3418

电气性能(Electrical properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (1MHz)	3.5 / 5.6	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (100Hz)	140 / 2300	E-4	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	140 / 1600	E-4	IEC 60250
体积电阻率(Volume resistivity)	1E13 / 1E10	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	* / 1E10	Ohm	IEC 60093
电气强度(Electric strength)	40 / 37	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	- / 550	-	IEC 60112
ASTM数据(ASTM Data)
体积电阻率(Volume Resistivity)	1E13	Ohm*cm	ASTM D 257

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	5.5 / *	%	Sim. to ISO 62
吸湿性(Humidity absorption)	1.7 / *	%	Sim. to ISO 62
密度(Density)	1360 / -	kg/m³	ISO 1183

材料特殊性能(Material specific properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
粘数(Viscosity number)	145 / *	cm³/g	ISO 307, 1157, 1628

流变计算属性(Rheological calculation properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
喷射温度(Ejection temperature)	195	°C	-

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	290	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724
Injection Molding, injection velocity	200	mm/s	ISO 294

Diagrams allowed water content: .15 % ISO 1817 Liquid F) (23°C)

ISO 1817 Liquid F) (>90°C)

Salt solutions

4 Brake fluid (130°C)