Ultramid® 7523-2AM BK ND3007|PA66-GF33|BASF物性表报告及物性特性介绍,Ultramid® 7523-2AM BK ND3007|PA66-GF33|BASF注塑参数详情-塑料物性表查询网

Product TextsUltramid® 7523-2AM BK ND3007 is an impact modified, 33% glass reinforced, heat stabilized injection molding PA6/6.

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	9200 / 8250	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	145 / 132	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	5 / 5	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	- / 94	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	- / 91	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	21 / 24	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	257 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	245 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	260 / *	°C	ISO 75-1/-2

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
密度(Density)	1330 / -	kg/m³	ISO 1183

CharacteristicsRegional AvailabilityNorth AmericaOther text informationInjection moldingPA66 materials must be properly dried in order to provide parts with optimum strength and toughness. PA66 materials are hygroscopic and will become degraded by excessive moisture during the injection molding process. For unopened bag/box, dry at 140F (60°C) for 1-2 hours. For material exposed to the atmosphere, if additional drying is needed, dry at 150F (66°C) or until the moisture level is between 0.04 - 0.20%.35 MPa (0 - 50 psi) Pac It should be applied and maintained until the gate area is completely frozen off.DisclaimerCopyright M-Base .