Tarnamid® T-30 MHS H2|PA6|Grupa Azoty

Tarnamid® T-30 MHS H2|PA6|Grupa Azoty 物性表: Tarnamid® T-30 MHS H2|PA6|Grupa Azoty物性表及特性介绍,Tarnamid® T-30 MHS H2|PA6|Grupa Azoty注塑参数详情,如需Tarnamid® T-30 MHS H2|PA6|Grupa Azoty下载, 可到相关下载区下载

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据
拉伸模量(Tensile Modulus)	2800 / -	MPa	ISO 527-1/-2
抗拉强度(Tensile Strength)	75 / -	MPa	ISO 527-1/-2
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	4.5 / -	kJ/m²	ISO 179/1eA
球压痕硬度(Ball indentation hardness)	130 / -	MPa	ISO 2039-1

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据
熔化温度(熔化温度(Melting temperature)) (10°C/min)	221 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	55 / *	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	175 / *	°C	ISO 306

CharacteristicsProcessingInjection MoldingDelivery formGranulesSpecial CharacteristicsU.V. stabilized or stable to weather, Heat stabilized or stable to heatRegional AvailabilityEuropeDisclaimerCopyright M-Base .