Technyl® C 218 MZ20 V10|PA6-MD30|Rhodia物性表报告及物性特性介绍,Technyl® C 218 MZ20 V10|PA6-MD30|Rhodia注塑参数详情-塑料物性表查询网

Technyl® C 218 MZ20 V10|PA6-MD30|Rhodia

Product TextsPolyamide PA6, reinforced 20 % mineral filler and 10 % of glass fibre. heat stabilised, for injection moulding.

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	7400 / 4500	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	100 / -	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	3.2 / -	%	ISO 527-1/-2
简支梁冲击强度(Charpy impact strength) (+23°C)	60 / -	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	6.8 / -	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	222 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	205 / *	°C	ISO 75-1/-2
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6 / *	mm	IEC 60695-11-10

Diagrams ISO 1817 Liquid C) (23°C)

ISO 1817 Liquid 4) (23°C)

Salt solutions