Ultramid® 8272G HS BK-102|PA6-GF12|BASF物性表报告及物性特性介绍,Ultramid® 8272G HS BK-102|PA6-GF12|BASF注塑参数详情-塑料物性表查询网

Product TextsUltramid® 8272G HS BK-102 is a 12% glass fiber reinforced, black pigmented, thermally modified, Polyamid 6 blow molding compound offering an excellent balance of engineering properties combined with the melt strength ideally suited for blow molding and other applications requiring ultra high melt viscosity. It exhibits improved strength, stiffness and creep resistance compare to standard blow molding grades. Outstanding permeability and chemical resistance to oils, hydrocarbons and most solventIt is ideal for air ducts, reservoirs and covers.

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	5220 / 3100	MPa	ISO 527-1/-2
屈服应力(Yield stress)	- / 65	MPa	ISO 527-1/-2
屈服应变(Yield strain)	- / 15	%	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	- / 20	%	ISO 527-1/-2

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	220 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	170 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	210 / *	°C	ISO 75-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	28 / *	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	72 / *	E-6/K	ISO 11359-1/-2

电气性能(Electrical properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
体积电阻率(Volume resistivity)	>1E13 / >1E13	Ohm*m	IEC 60093

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	8.3 / *	%	Sim. to ISO 62
吸湿性(Humidity absorption)	2.3 / *	%	Sim. to ISO 62
密度(Density)	1220 / *	kg/m³	ISO 1183

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	275	°C	ISO 294
Injection Molding, mold temperature	95	°C	ISO 10724

Diagrams Water content: 0.15%If drying Drying time is The degree of crystallinity of thin 6mm (.023") or less, may be controlled A cold mold, 5-30 degC (41-86 degF), As part complexity increases, lower DisclaimerCopyright M-Base .