Ultramid® 8262G HS BK-102|PA6-(MD+GF)20|BASF物性表报告及物性特性介绍,Ultramid® 8262G HS BK-102|PA6-(MD+GF)20|BASF注塑参数详情-塑料物性表查询网

Product TextsUltramid® 8262G HS BK-102 is a heat stabilized, pigmented black, 20% glass and mineral reinforced Polyamid 6 injection molding compound resulting in a balance of engineering properties with excellent dimensional stability, low warp and good resistance to sink mark formation.

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	5200 / -	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	100 / -	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	3 / -	%	ISO 527-1/-2
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	3 / -	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	220 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	163 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	211 / *	°C	ISO 75-1/-2
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	3.0 / *	mm	IEC 60695-11-10
UL 识别(recognition)	UL / *	-	-

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	7.9 / *	%	Sim. to ISO 62
吸湿性(Humidity absorption)	2.2 / *	%	Sim. to ISO 62
密度(Density)	1290 / *	kg/m³	ISO 1183

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	275	°C	ISO 294
Injection Molding, mold temperature	95	°C	ISO 10724

CharacteristicsProcessingInjection MoldingDelivery formPelletsSpecial CharacteristicsHeat stabilized or stable to heatRegional AvailabilityNorth AmericaOther text informationInjection moldingPREPROCESSING Water content: 0.12% If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level. Alternatively, please contact your BASF representative. Packing pressure affects the final part and can be use It should be applied and maintained until the gate area is completely frozen off.A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Surface appearance is directly affected by injection rateDisclaimerCopyright M-Base .