Ultramid® B3ZG6|PA6-I-GF30|BASF物性表报告及物性特性介绍,Ultramid® B3ZG6|PA6-I-GF30|BASF注塑参数详情-塑料物性表查询网

Product TextsAn impact-modified, glass fibre reinforced injection molding grade for industrial items requiring very high impact stregth and rigidity, used e.g. for automobile airbag housings and half-shells for suitcases.

流变性能(Rheological properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔体体积流动速率(Melt volume-flow rate) (MVR)	20 / *	cm³/10min	ISO 1133
温度(Temperature)	275 / *	°C	ISO 1133
负载(Load)	5 / *	kg	ISO 1133
成型收缩(Molding shrinkage) (parallel)	0.3 / *	%	ISO 294-4, 2577
成型收缩(Molding shrinkage) (normal)	0.7 / *	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	9000 / 5300	MPa	ISO 527-1/-2
破坏时应变(Stress at break)	150 / 100	MPa	ISO 527-1/-2
破坏时应变(Strain at break)	3.6 / 10	%	ISO 527-1/-2
Tensile creep modulus (1h)	* / 3800	MPa	ISO 899-1
Tensile creep modulus (1000h)	* / 3000	MPa	ISO 899-1
简支梁冲击强度(Charpy impact strength) (+23°C)	95 / 110	kJ/m²	ISO 179/1eU
简支梁冲击强度(Charpy impact strength) (-30°C)	90 / 101	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度(Charpy notched impact strength) (+23°C)	20 / 35	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度(Charpy notched impact strength) (-30°C)	15 / 9.7	kJ/m²	ISO 179/1eA

热性能(热性能(Thermal properties))	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
熔化温度(熔化温度(Melting temperature)) (10°C/min)	220 / *	°C	ISO 11357-1/-3
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	200 / *	°C	ISO 75-1/-2
温度负荷变形(Temp. of deflection under load) (0.45 MPa)	220 / *	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	220 / *	°C	ISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	22.5 / *	E-6/K	ISO 11359-1/-2
COEFF线性热(Coeff. of linear therm. expansion) (normal)	65 / *	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.6 / *	mm	IEC 60695-11-10
UL 识别(recognition)	UL / *	-	-
燃烧性(球压痕硬度(Burning behav)). at thickness h	HB / *	class	IEC 60695-11-10
厚度测试(Thickness tested)	0.7 / *	mm	IEC 60695-11-10
UL 识别(recognition)	UL / *	-	-
Oxygen index	23 / *	%	ISO 4589-1/-2

电气性能(Electrical properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (1MHz)	3.8 / 6.8	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (100Hz)	200 / 2200	E-4	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	200 / 2000	E-4	IEC 60250
体积电阻率(Volume resistivity)	1E13 / 1E10	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	* / 1E10	Ohm	IEC 60093
电气强度(Electric strength)	46 / 38	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	- / 550	-	IEC 60112

其他属性(Other properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	6.2 / *	%	Sim. to ISO 62
吸湿性(Humidity absorption)	2 / *	%	Sim. to ISO 62
密度(Density)	1330 / -	kg/m³	ISO 1183

材料特殊性能(Material specific properties)	dry / cond	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
粘数(Viscosity number)	160 / *	cm³/g	ISO 307, 1157, 1628

流变计算属性(Rheological calculation properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
喷射温度(Ejection temperature)	160	°C	-

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	280	°C	ISO 294
Injection Molding, mold temperature	80	°C	ISO 10724
Injection Molding, injection velocity	200	mm/s	ISO 294

Diagrams allowed water content: .15 % ISO 1817 Liquid F) (23°C)

ISO 1817 Liquid F) (>90°C)

Salt solutions

4 Brake fluid (130°C)