XANTAR® MX 2032|PC|Mitsubishi EP物性表报告及物性特性介绍,XANTAR® MX 2032|PC|Mitsubishi EP注塑参数详情-塑料物性表查询网

Product TextsHigh Flow2	kg	ISO 1133
成型收缩(Molding shrinkage) (parallel)	0.6	%	ISO 294-4, 2577

机械性能(机械性能(Mechanical properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	2300	MPa	ISO 527-1/-2
屈服应力(Yield stress)	60	MPa	ISO 527-1/-2
屈服应变(Yield strain)	6	%	ISO 527-1/-2
断裂拉伸应变(Nominal strain at break)	>50	%	ISO 527-1/-2

热性能(热性能(Thermal properties))	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
温度负荷变形(Temp. of deflection under load) (1.80 MPa)	135	°C	ISO 75-1/-2
维卡软化温度（50℃/ h的50N）Vicat softening temperature	145	°C	ISO 306
COEFF线性热(Coeff. of linear therm. expansion) (parallel)	65	E-6/K	ISO 11359-1/-2
燃烧性(球压痕硬度(Burning behav)). at 1.5 mm nom. thickn.	V-2	class	IEC 60695-11-10
厚度测试(Thickness tested)	1.5	mm	IEC 60695-11-10
Oxygen index	26	%	ISO 4589-1/-2

电气性能(Electrical properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
相对介电常数(Relative permittivity) (100Hz)	2.9	-	IEC 60250
相对介电常数(Relative permittivity) (1MHz)	2.8	-	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (100Hz)	6.6	E-4	IEC 60250
耗散因数(耗散因数(Dissipation factor)) (1MHz)	92	E-4	IEC 60250
体积电阻率(Volume resistivity)	>1E13	Ohm*m	IEC 60093
表面电阻率(Surface resistivity)	>1E15	Ohm	IEC 60093
电气强度(Electric strength)	29	kV/mm	IEC 60243-1
相比漏电起痕指数(Comparative tracking index)	225	-	IEC 60112

其他属性(Other properties)	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
吸水率(Water absorption)	0.35	%	Sim. to ISO 62
密度(Density)	1200	kg/m³	ISO 1183

Test specimen production	值(Value)	单位(Unit)	测试标准(Test Standard)
ISO数据(ISO数据(CAMPUS/ISO) Data)
Injection Molding, melt temperature	300	°C	ISO 294
Injection Molding, mold temperature	90	°C	ISO 10724

CharacteristicsProcessingInjection MoldingDelivery formPelletsSpecial CharacteristicsLight stabilized or stable to light, U.V. stabilized or stable to weather, Heat stabilized or stable to heat, TransparentRegional AvailabilityEuropeOther text informationInjection moldingInjection Molding RecommendationsDisclaimerCopyright M-Base .
[/td][/tr][/table]