- 密度 [g/cm3]: 1.11
- 吸水率 [%]: 0.19
- 缺口冲击强度: 0.8
- 断裂伸长率 [%]: 41.0
- 弯曲强度 [MPa]: 41.0
- 弯曲模量 [MPa]: 2.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ASTM D792 |
| Water Absorption | 0.19 % | 0.19 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm @Thickness 3.17 mm | 0.0040 - 0.0060 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
| Elongation at Break | 2.0 - 5.0 % | 2.0 - 5.0 % | ASTM D638 |
| Tensile Modulus | 2.60 GPa | 377 ksi | ASTM D638 |
| Flexural Yield Strength | 41.0 MPa | 5950 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 - 1.33 J/cm @Thickness 6.35 mm | 1.50 - 2.49 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 216 - 243 °C | 421 - 469 °F | Stock |
| Mold Temperature | 49.0 - 66.0 °C | 120 - 151 °F | |
| Drying Temperature | 60.0 - 71.0 °C | 140 - 160 °F | |