- 缺口冲击强度: 1.07
- 弯曲强度 [MPa]: 89.6
- 弯曲模量 [MPa]: 10.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Elongation at Break | 5.0 % | 5.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Tensile Modulus | 10.3 GPa | 1500 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 | ||
| Flexural Modulus | 10.3 GPa | 1500 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 2.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.0 - 5.0 ohm-cm | 1.0 - 5.0 ohm-cm | ASTM D257 | ||
| Surface Resistivity per Square | 1.0 - 5.0 ohm | 1.0 - 5.0 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Annealed, 0.125 in bars; ASTM D648 | ||
| Descriptive Properties | |||||
| Shielding Effectiveness | 40 - 70 db | 1,000 MHz | |||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.