- 熔体流动速率 [g/10min]: 3.92
- 密度 [g/cm3]: 0.929
- 拉伸强度 [MPa]: 6.5
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.929 g/cc | 0.0336 lb/in³ | |
| Melt Flow | 3.92 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.92 g/10 min @Load 4.76 lb, Temperature 374 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 6.50 MPa | 943 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Tensile Modulus | 0.100 GPa | 14.5 ksi | 1 mm/min |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 98.0 °C | 208 °F | 10°C/min |
| Vicat Softening Point | 77.0 °C | 171 °F | 50°C/hr; 50N |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 80 % | 80 % | Mfr. reports 'Transparent' but doesn't quantify. |