- 熔体流动速率 [g/10min]: 5.1
- 密度 [g/cm3]: 0.935
- 拉伸强度 [MPa]: 5.0
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | |
| Melt Flow | 5.1 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.1 g/10 min @Load 4.76 lb, Temperature 374 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 5.00 MPa | 725 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Tensile Modulus | 0.0750 GPa | 10.9 ksi | 1 mm/min |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 92.0 °C | 198 °F | 10°C/min |
| Vicat Softening Point | 68.0 °C | 154 °F | 50°C/hr; 50N |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 80 % | 80 % | Mfr. reports 'Transparent' but doesn't quantify. |