- 密度 [g/cm3]: 0.94
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc @Temperature 23.0 °C | 0.0340 lb/in³ @Temperature 73.4 °F | ISO 1183 |
| Vinyl Acetate Content | 19 - 21 % | 19 - 21 % | FTIR (internal) |
| Melt Index of Compound | 17 - 23 g/10 min @Load 2.16 kg, Temperature 190 °C | 17 - 23 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 82 | 82 | ASTM D2240 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
| Elongation at Break | 600 - 900 % | 600 - 900 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 82.0 °C | 180 °F | DSC |
| Vicat Softening Point | 47.0 °C @Load 0.999 kg | 117 °F @Load 2.20 lb | ISO 306 |
| Ring & Ball Softening Point | 127 °C | 261 °F | ASTM E28 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | <= 230 °C | <= 446 °F | |