- 密度 [g/cm3]: 0.95
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc @Temperature 23.0 °C | 0.0343 lb/in³ @Temperature 73.4 °F | ISO 1183 |
| Vinyl Acetate Content | 26 - 28 % | 26 - 28 % | FTIR (internal) |
| Melt Index of Compound | 3.0 - 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.0 - 4.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 82 | 82 | ASTM D2240 |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | 700 - 1000 % | 700 - 1000 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 76.0 °C | 169 °F | DSC |
| Vicat Softening Point | 41.0 °C @Load 0.999 kg | 106 °F @Load 2.20 lb | ISO 306 |
| Ring & Ball Softening Point | 166 °C | 331 °F | ASTM E28 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | <= 230 °C | <= 446 °F | |