- 密度 [g/cm3]: 0.951
- 拉伸强度 [MPa]: 1.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | ASTM D1505 | ||
| Vinyl Acetate Content | 26 - 30 % | 26 - 30 % | Arkema | ||
| Melt Index of Compound | 150 - 210 g/10 min @Load 2.16 kg, Temperature 190 °C | 150 - 210 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 71 | 71 | ASTM D2240 | ||
| Tensile Strength at Break | 4.50 MPa | 653 psi | ASTM D638 | ||
| Tensile Strength, Yield | 1.80 MPa | 261 psi | ASTM D638 | ||
| Elongation at Break | 700 - 900 % | 700 - 900 % | ASTM D638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 68.0 °C | 154 °F | DSC | ||
| Vicat Softening Point | <= 40.0 °C | <= 104 °F | ASTM D1525 | ||
| Ring & Ball Softening Point | 92.0 °C | 198 °F | |||
| Descriptive Properties | |||||
| MAH Mini | 6400 | ||||