- 密度 [g/cm3]: 0.95
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc @Temperature 23.0 °C | 0.0343 lb/in³ @Temperature 73.4 °F | ISO 1183 |
| Vinyl Acetate Content | 27 - 29 % | 27 - 29 % | FTIR (internal) |
| Melt Index of Compound | 5.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 80 | 80 | ASTM D2240 |
| Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D638 |
| Elongation at Break | 700 - 1000 % | 700 - 1000 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 72.0 °C | 162 °F | DSC |
| Vicat Softening Point | 40.0 °C @Load 0.999 kg | 104 °F @Load 2.20 lb | ISO 306 |
| Ring & Ball Softening Point | 160 °C | 320 °F | ASTM E28 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | <= 230 °C | <= 446 °F | |