- 密度 [g/cm3]: 0.932
- 拉伸强度 [MPa]: 6.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | ASTM D1505 | ||
| Vinyl Acetate Content | 8.0 - 9.5 % | 8.0 - 9.5 % | Arkema | ||
| Melt Index of Compound | 3.3 - 4.7 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.3 - 4.7 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 91 | 91 | ASTM D2240 | ||
| Tensile Strength at Break | 18.0 MPa | 2610 psi | ASTM D638 | ||
| 22.0 MPa | 3190 psi | Film Property, 50 µm thickness; ASTM D882 | |||
| Tensile Strength, Yield | 6.00 MPa | 870 psi | ASTM D638 | ||
| 6.00 MPa | 870 psi | Film Property, 50 µm thickness; ASTM D882 | |||
| Elongation at Break | 500 - 700 % | 500 - 700 % | Film Property, 50 µm thickness; ASTM D882 | ||
| 600 - 900 % | 600 - 900 % | ASTM D638 | |||
| Dart drop Test | 355 g | 0.783 lb | ASTM D1709 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 105 °C | 221 °F | DSC | ||
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 | ||
| Ring & Ball Softening Point | 182 °C | 360 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Haze | 7.6 % | 7.6 % | 50 micron film; ASTM D1003 | ||
| Descriptive Properties | |||||
| MAH Mini | 1600 | ||||