- 熔体流动速率 [g/10min]: 400.0
- 密度 [g/cm3]: 0.941
- 弯曲模量 [MPa]: 0.00870
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.941 g/cc | 0.0340 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 28 % | 28 % | AT Plastics PTM-39 |
| Melt Flow | 400 g/10 min @Load 0.325 kg, Temperature 125 °C | 400 g/10 min @Load 0.716 lb, Temperature 257 °F | Modified; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 68 | 68 | ASTM D2240 |
| Tensile Strength at Break | 3.50 MPa | 508 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 900 % | 900 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.00870 GPa | 1.26 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Ring & Ball Softening Point | 84.0 °C | 183 °F | ASTM E28 |