- 熔体流动速率 [g/10min]: 30.0
- 密度 [g/cm3]: 0.934
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 19 % | 19 % | AT Plastics PTM-39 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 190 °C | 30 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 4.00 MPa | 580 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Yield, TD | 4.00 MPa | 580 psi | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, MD | 520 % | 520 % | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, TD | 610 % | 610 % | Method A (500 mm/min); ASTM D882 |
| Dart Drop | 3.40 g/micron | 86.4 g/mil | f50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 15.0 MPa | 2180 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Break, TD | 13.0 MPa | 1890 psi | Method A (500 mm/min); ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 87.0 °C | 189 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 51.0 °C | 124 °F | ASTM D1525 |