- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.932
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | ASTM D1505; ASTM D1928 Proc A | ||
| Vinyl Acetate Content | 12 % | 12 % | AT Plastics PTM-39 | ||
| Thickness | 75.0 microns | 2.95 mil | |||
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 7.00 MPa | 1020 psi | Method A (500 mm/min); ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 6.00 MPa | 870 psi | Method A (500 mm/min); ASTM D882 | ||
| Film Elongation at Break, MD | 400 % | 400 % | Method A (500 mm/min); ASTM D882 | ||
| Film Elongation at Break, TD | 510 % | 510 % | Method A (500 mm/min); ASTM D882 | ||
| Dart Drop | 6.00 g/micron | 152 g/mil | f50; ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 27.0 MPa | 3920 psi | Method A (500 mm/min); ASTM D882 | ||
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | Method A (500 mm/min); ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 97.0 °C | 207 °F | DSC; ASTM D3417 | ||
| Vicat Softening Point | 78.0 °C | 172 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 13 % | 13 % | ASTM D1003 | ||
| Gloss | 38 % | 38 % | 45°; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Blow-up Ratio (BUR) | 2.1 | 2.1 | |||
| Descriptive Properties | |||||
| Process | Extrusion | ||||
| region | US & Canada | ||||