- 熔体流动速率 [g/10min]: 15.0
- 密度 [g/cm3]: 0.941
- 弯曲模量 [MPa]: 0.0360
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.941 g/cc | 0.0340 lb/in³ | ASTM D1505; ASTM D1928 Proc A | ||
| Vinyl Acetate Content | 20 % | 20 % | AT Plastics PTM-39 | ||
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 190 °C | 15 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 90 | 90 | ASTM D2240 | ||
| Hardness, Shore D | 32 | 32 | ASTM D2240 | ||
| Tensile Strength at Break | 9.00 MPa | 1310 psi | Type IV (50 mm/min); ASTM D638 | ||
| Elongation at Break | 675 % | 675 % | Type IV (50 mm/min); ASTM D638 | ||
| Flexural Modulus | 0.0360 GPa | 5.22 ksi | 1% Secant; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 84.0 °C | 183 °F | DSC; ASTM D3417 | ||
| Vicat Softening Point | 53.0 °C | 127 °F | ASTM D1525 | ||
| Brittleness Temperature | -76.0 °C | -105 °F | ASTM D746 | ||
| Descriptive Properties | |||||
| Process | Extrusion | ||||
| Injection Molding | |||||
| region | US & Canada | ||||