- 熔体流动速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.93
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D792 |
| Melt Flow | 0.35 g/10 min | 0.35 g/10 min | Condition not noted.; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 620 % | 620 % | MD-TD Average; ASTM D882 |
| Film Elongation at Break, TD | 620 % | 620 % | MD-TD Average; ASTM D882 |
| Impact | 36.9 | 36.9 | J/mm Spencer Impact; Average of MD and TD; ASTM D3420 |
| Elmendorf Tear Strength, MD | 1.77 g/micron | 45.0 g/mil | Average of MD and TD; ASTM D1922 |
| Film Tensile Strength at Break, MD | 33.7 MPa | 4890 psi | MD-TD Average; ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 82.0 °C | 180 °F | Freezing Point via DSC/ASTM D3418 |
| 100 °C | 212 °F | Upon Melting via DSC/ASTM D3418 | |
| Vicat Softening Point | 87.0 °C | 189 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.0 % | 2.0 % | ASTM D1003 |
| Gloss | 121 % | 121 % | 20°; ASTM D2457 |