- 密度 [g/cm3]: 0.951
- 弯曲强度 [MPa]: 14.0
- 弯曲模量 [MPa]: 0.0160
- 脆化温度 [℃]: -100.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | ASTM D792 | ||
| Vinyl Acetate Content | 28 % | 28 % | TGA | ||
| Melt Index of Compound | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 85 | 85 | ASTM D2240 | ||
| Hardness, Shore D | 33 | 33 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | Type IV, crosshead speed 2 in/min; ASTM D638 | ||
| 3.40 MPa @Temperature 49.0 °C | 493 psi @Temperature 120 °F | Type IV, crosshead speed 2 in/min; ASTM D638 | |||
| 33.0 MPa @Temperature -20.0 °C | 4790 psi @Temperature -4.00 °F | Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 | |||
| Elongation at Break | 800 % | 800 % | Type IV, crosshead speed 2 in/min; ASTM D638 | ||
| 450 % @Temperature -20.0 °C | 450 % @Temperature -4.00 °F | Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 | |||
| 700 % @Temperature 49.0 °C | 700 % @Temperature 120 °F | Type IV, crosshead speed 2 in/min; ASTM D638 | |||
| Modulus of Elasticity | 0.0130 GPa | 1.89 ksi | |||
| 0.0630 GPa @Temperature -20.0 °C | 9.14 ksi @Temperature -4.00 °F | ||||
| Flexural Modulus | 0.0160 GPa | 2.32 ksi | ASTM D790 | ||
| 0.0100 GPa @Temperature 49.0 °C | 1.45 ksi @Temperature 120 °F | ASTM D790 | |||
| 0.0940 GPa @Temperature -20.0 °C | 13.6 ksi @Temperature -4.00 °F | ASTM D790 | |||
| Flexural Stiffness | 13.0002 MPa | 1885.52 psi | |||
| 63.0010 MPa @Temperature -20.0 °C | 9137.52 psi @Temperature -4.00 °F | ||||
| Tensile Impact Strength | 565 kJ/m² | 269 ft-lb/in² | At -20°C; ASTM D1822 | ||
| 755 kJ/m² | 359 ft-lb/in² | At 23°C; ASTM D1822 | |||
| Compression Set | 55 % | 55 % | Method B, 10 days at 25°C; ASTM D395 | ||
| 100 % @Temperature 70.0 °C | 100 % @Temperature 158 °F | Method B, 22 hours; ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 47.0 °C | 117 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D762 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 121 - 204 °C | 250 - 399 °F | |||
| Descriptive Properties | |||||
| Cycle time | 0.5-2 minutes | Molding, equipment and part design dependent | |||
| Vinyl Acetate Content | 28 wt.% | ||||