- 密度 [g/cm3]: 0.93
- 弯曲强度 [MPa]: 14.0
- 弯曲模量 [MPa]: 0.0830
- 脆化温度 [℃]: -100.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D792 | ||
| Vinyl Acetate Content | 7.0 % | 7.0 % | TGA | ||
| Melt Index of Compound | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 95 | 95 | ASTM D2240 | ||
| Hardness, Shore D | 46 | 46 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | Type IV, crosshead speed 2 in/min; ASTM D638 | ||
| 9.00 MPa @Temperature 49.0 °C | 1310 psi @Temperature 120 °F | Type IV, crosshead speed 2 in/min; ASTM D638 | |||
| 20.0 MPa @Temperature -20.0 °C | 2900 psi @Temperature -4.00 °F | Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 | |||
| Elongation at Break | 600 % | 600 % | Type IV, crosshead speed 2 in/min; ASTM D638 | ||
| 500 % @Temperature -20.0 °C | 500 % @Temperature -4.00 °F | Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 | |||
| 600 % @Temperature 49.0 °C | 600 % @Temperature 120 °F | Type IV, crosshead speed 2 in/min; ASTM D638 | |||
| Modulus of Elasticity | 0.0800 GPa | 11.6 ksi | |||
| 0.204 GPa @Temperature -20.0 °C | 29.6 ksi @Temperature -4.00 °F | ||||
| Flexural Modulus | 0.0830 GPa | 12.0 ksi | ASTM D790 | ||
| 0.0450 GPa @Temperature 49.0 °C | 6.53 ksi @Temperature 120 °F | ASTM D790 | |||
| 0.361 GPa @Temperature -20.0 °C | 52.4 ksi @Temperature -4.00 °F | ASTM D790 | |||
| Flexural Stiffness | 80.0012 MPa | 11603.2 psi | |||
| 204.0 MPa @Temperature -20.0 °C | 29590 psi @Temperature -4.00 °F | ||||
| Tensile Impact Strength | 335 kJ/m² | 159 ft-lb/in² | At -20°C; ASTM D1822 | ||
| 400 kJ/m² | 190 ft-lb/in² | At 23°C; ASTM D1822 | |||
| Compression Set | 45 % | 45 % | Method B, 10 days at 25°C; ASTM D395 | ||
| 80 % @Temperature 70.0 °C | 80 % @Temperature 158 °F | Method B, 22 hours; ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 73.0 °C | 163 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D762 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 121 - 204 °C | 250 - 399 °F | |||
| Descriptive Properties | |||||
| Cycle time | 0.5-2 minutes | Molding, equipment and part design dependent | |||
| Vinyl Acetate Content | 7 wt.% | ||||