- 熔体流动速率 [g/10min]: 12.0
- 拉伸强度 [MPa]: 4.0
- 弯曲模量 [MPa]: 0.0400
- 脆化温度 [℃]: -80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.941 g/cc | 0.941 g/cc | ISO 1183 |
| Vinyl Acetate Content | 19 % | 19 % | Internal Method |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 190 °C | 12 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 89 | 89 | ISO 868/A |
| Hardness, Shore D | 33 | 33 | ISO 868/A |
| Tensile Strength, Yield | 4.00 MPa | 580 psi | ISO 527 |
| Flexural Modulus | 0.0400 GPa | 5.80 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 83.0 °C | 181 °F | Internal Method |
| Vicat Softening Point | 56.0 °C @Load 1.00 kg | 133 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -80.0 °C | <= -112 °F | ASTM D746 |