- 熔体流动速率 [g/10min]: 3.1
- 密度 [g/cm3]: 0.931
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.931 g/cc | 0.0336 lb/in³ | ASTM D1505 |
| Water Vapor Transmission | 54.0 g/m²/day | 3.48 g/100 in²/day | 100% Humidity; ASTM F372 |
| Thickness | 50.8 microns | 2.00 mil | 2:1 BUR |
| Melt Flow | 3.1 g/10 min | 3.1 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.7 MPa | 1840 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.20 MPa | 1040 psi | ASTM D882 |
| Film Elongation at Break, MD | 380 % | 380 % | ASTM D882 |
| Film Elongation at Break, TD | 647 % | 647 % | ASTM D882 |
| Film Elongation at Yield, MD | 62 % | 62 % | ASTM D882 |
| Film Elongation at Yield, TD | 64 % | 64 % | ASTM D882 |
| Elmendorf Tear Strength MD | 292 g | 292 g | Notched; ASTM D1922 |
| Elmendorf Tear Strength TD | 232 g | 232 g | Notched; ASTM D1922 |
| Elmendorf Tear Strength, MD | 5.75 g/micron | 146 g/mil | based on 2 mil film; ASTM D1922 |
| Elmendorf Tear Strength, TD | 6.54 g/micron | 166 g/mil | based on 2 mil film; ASTM D1922 |
| Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.3 MPa | 3230 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 78.0 °C | 172 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | >= 210 °C | >= 410 °F | |