- 熔体流动速率 [g/10min]: 3.7
- 密度 [g/cm3]: 0.931
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.931 g/cc | 0.0336 lb/in³ | ASTM D1505 |
| Water Vapor Transmission | 60.8 g/m²/day | 3.92 g/100 in²/day | 100% Humidity; ASTM F372 |
| Thickness | 50.8 microns | 2.00 mil | 2:1 BUR |
| Melt Flow | 3.7 g/10 min | 3.7 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 4.20 MPa | 609 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.40 MPa | 1070 psi | ASTM D882 |
| Film Elongation at Break, MD | 710 % | 710 % | ASTM D882 |
| Film Elongation at Break, TD | 460 % | 460 % | ASTM D882 |
| Film Elongation at Yield, MD | 14 % | 14 % | ASTM D882 |
| Film Elongation at Yield, TD | 28 % | 28 % | ASTM D882 |
| Elmendorf Tear Strength MD | 94 g | 94 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 418 g | 418 g | ASTM D1922 |
| Film Tensile Strength at Break, MD | 24.3 MPa | 3520 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 27.2 MPa | 3950 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 58.0 °C | 136 °F | ASTM D1525 |