- 熔体流动速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.933
- 拉伸强度 [MPa]: 5.52
- 弯曲模量 [MPa]: 0.0600
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.933 g/cc | 0.0337 lb/in³ | ExxonMobil Method |
| Vinyl Acetate Content | 14.4 % | 14.4 % | ExxonMobil Method |
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | 190°C, 2.16 kg; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 83 | 83 | 15s; ASTM D2240 |
| Hardness, Shore D | 33 | 33 | 15s; ASTM D2240 |
| Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D638 |
| Tensile Strength, Yield | 5.52 MPa | 800 psi | ASTM D638 |
| Elongation at Break | 750 % | 750 % | ASTM D638 |
| Elongation at Yield | 170 % | 170 % | ASTM D638 |
| Flexural Modulus | 0.0600 GPa | 8.70 ksi | 1% secant; ASTM D790 |
| Impact Test | 14.9 J | 11.0 ft-lb | Instrument Impact, Total Energy at 23°C; ASTM D3763 |
| 29.8 J | 22.0 ft-lb | Instrument Impact, Total Energy at -40°C; ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 87.8 °C | 190 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 62.8 °C | 145 °F | ASTM D1525 |