- 熔体流动速率 [g/10min]: 1.25
- 密度 [g/cm3]: 0.924
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ExxonMobil Method | ||
| Vinyl Acetate Content | 4.2 % | 4.2 % | ExxonMobil Method | ||
| Melt Flow | 1.25 g/10 min | 1.25 g/10 min | ExxonMobil Method | ||
| Antiblock Level | 4000 ppm | 4000 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.07 MPa | 1170 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 7.65 MPa | 1110 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 180 % | 180 % | ASTM D882 | ||
| Film Elongation at Break, TD | 580 % | 580 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 7.0 % | 7.0 % | ASTM D882 | ||
| Film Elongation at Yield, TD | 5.5 % | 5.5 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 170 g | 170 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 90 g | 90 g | ASTM D1922 | ||
| Dart drop Test | 180 g | 0.397 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 24.3 MPa | 3530 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 23.2 MPa | 3360 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 141 MPa | 20400 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 163 MPa | 23700 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 104 °C | 220 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 91.0 °C | 196 °F | ExxonMobil Method | ||
| Vicat Softening Point | 87.2 °C | 189 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 7.4 % | 7.4 % | ASTM D1003 | ||
| Gloss | 68 % | 68 % | 45°; ASTM D2457 | ||
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||