ExxonMobil Escorene® LD 705.MJ Molding, extrusion and compounding resin

ExxonMobil Escorene® LD 705.MJ Molding, extrusion and compounding resin 物性表: ExxonMobil Escorene® LD 705.MJ Molding, extrusion and compounding resin物性表及特性介绍,ExxonMobil Escorene® LD 705.MJ Molding, extrusion and compounding resin注塑参数详情,如需ExxonMobil Escorene® LD 705.MJ Molding, extrusion and compounding resin下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 0.4
  • 密度 [g/cm3]: 0.934
  • 拉伸强度 [MPa]: 6.31
  • 弯曲模量 [MPa]: 0.0876
 
Physical PropertiesMetricEnglishComments
Density 0.934 g/cc0.0337 lb/in³ExxonMobil Method
Vinyl Acetate Content 13.3 %13.3 %ExxonMobil Method
Melt Flow 0.40 g/10 min0.40 g/10 min190 °C, 2.16 kg; ASTM D1238
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore A 777715s; ASTM D2240
Hardness, Shore D 393915s; ASTM D2240
Tensile Strength at Break 15.5 MPa2250 psiASTM D638
Tensile Strength, Yield 6.31 MPa915 psiASTM D638
Elongation at Break >= 800 %>= 800 %ASTM D638
Elongation at Yield 180 %180 %ASTM D638
Flexural Modulus 0.0876 GPa12.7 ksi1% secant; ASTM D790
Impact Test 19.0 J14.0 ft-lbInstrument Impact, Total Energy at 23°C; ASTM D3763
 32.5 J24.0 ft-lbInstrument Impact, Total Energy at -40°C; ASTM D3763
 
Thermal PropertiesMetricEnglishComments
Melting Point 93.9 °C201 °FPeak Melting Temperature; ExxonMobil Method
Vicat Softening Point 77.2 °C171 °FASTM D1525

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-29651.html

免责声明: 本文 ExxonMobil Escorene® LD 705.MJ Molding, extrusion and compounding resin 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4