- 熔体流动速率 [g/10min]: 135.0
- 密度 [g/cm3]: 0.935
- 弯曲强度 [MPa]: 3.4
- 弯曲模量 [MPa]: 0.0340
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | Exxon Method |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50, Condition A; ASTM D1693 |
| Melt Flow | 135 g/10 min | 135 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 76 | 76 | ASTM D2240 |
| Hardness, Shore D | 26 | 26 | ASTM D2240 |
| Tensile Strength, Ultimate | 3.40 MPa | 493 psi | ASTM D638 |
| Elongation at Break | 450 % | 450 % | ASTM D638 |
| Flexural Modulus | 0.0340 GPa | 4.93 ksi | 1% Secant, ASTM D790 |
| Tensile Impact Strength | 146 kJ/m² | 69.5 ft-lb/in² | 23°C; ASTM D-1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 84.0 °C | 183 °F | Exxon Method |
| Vicat Softening Point | 44.0 °C | 111 °F | 1000g; ASTM D-1525 |