- 熔体流动速率 [g/10min]: 30.0
- 密度 [g/cm3]: 0.94
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 30 g/10 min | 30 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 5.20 MPa | 754 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 3.90 MPa | 566 psi | ASTM D882 |
| Film Elongation at Break, MD | 340 % | 340 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Secant Modulus, MD | 0.0560 GPa | 8.12 ksi | ASTM D882 |
| Secant Modulus, TD | 0.0620 GPa | 8.99 ksi | ASTM D882 |
| Impact Test | 1.50 J | 1.11 ft-lb | Total Energy Dart, 23°C |
| Elmendorf Tear Strength, MD | 5.91 g/micron | 150 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 6.69 g/micron | 170 g/mil | ASTM D1922 |
| Dart Drop | 1.93 g/micron | 49.0 g/mil | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 21.0 MPa | 3050 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 12.0 MPa | 1740 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 85.0 °C | 185 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 5.1 % | 5.1 % | ASTM D1003 |
| Gloss | 80 % | 80 % | 45°, ASTM D-2457 |