- 熔体流动速率 [g/10min]: 8.3
- 密度 [g/cm3]: 0.935
- 弯曲强度 [MPa]: 9.6
- 弯曲模量 [MPa]: 0.0550
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | Exxon Method |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50, Condition A; ASTM D1693 |
| Melt Flow | 8.3 g/10 min | 8.3 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 80 | 80 | ASTM D2240 |
| Hardness, Shore D | 29 | 29 | ASTM D2240 |
| Tensile Strength, Ultimate | 9.60 MPa | 1390 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 0.0550 GPa | 7.98 ksi | 1% Secant, ASTM D790 |
| Tensile Impact Strength | 324 kJ/m² | 154 ft-lb/in² | 23°C; ASTM D-1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 90.0 °C | 194 °F | Exxon Method |
| Vicat Softening Point | 61.0 °C | 142 °F | 1000g; ASTM D-1525 |