- 熔体流动速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.95
- 弯曲强度 [MPa]: 17.0
- 弯曲模量 [MPa]: 0.0260
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | Exxon Method |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50, Condition A; ASTM D1693 |
| Melt Flow | 2.3 g/10 min | 2.3 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 76 | 76 | ASTM D2240 |
| Hardness, Shore D | 26 | 26 | ASTM D2240 |
| Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 0.0260 GPa | 3.77 ksi | 1% Secant, ASTM D790 |
| Tensile Impact Strength | 805 kJ/m² | 383 ft-lb/in² | 23°C; ASTM D-1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 73.0 °C | 163 °F | Exxon Method |
| Vicat Softening Point | 51.0 °C | 124 °F | 1000g; ASTM D-1525 |