- 熔体流动速率 [g/10min]: 2.1
- 密度 [g/cm3]: 0.926
- 拉伸强度 [MPa]: 7.6
- 弯曲强度 [MPa]: 16.0
- 弯曲模量 [MPa]: 0.140
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | Exxon Method |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F50, Condition C; ASTM D1693 |
| Melt Flow | 2.1 g/10 min | 2.1 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 33 | 33 | ASTM D2240 |
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ASTM D638 |
| Tensile Strength, Yield | 7.60 MPa | 1100 psi | ASTM D638 |
| Elongation at Break | 1300 % | 1300 % | ASTM D638 |
| Flexural Modulus | 0.140 GPa | 20.3 ksi | 1% Secant, ASTM D790 |
| Tensile Impact Strength | 2.50 kJ/m² | 1.19 ft-lb/in² | 23°C; ASTM D-1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 96.0 °C | 205 °F | Exxon Method |