- 熔体流动速率 [g/10min]: 25.0
- 密度 [g/cm3]: 0.954
- 弯曲强度 [MPa]: 6.2
- 弯曲模量 [MPa]: 0.00900
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in³ | Exxon Method |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50, Condition A; ASTM D1693 |
| Melt Flow | 25 g/10 min | 25 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 58 | 58 | ASTM D2240 |
| Hardness, Shore D | 15 | 15 | ASTM D2240 |
| Tensile Strength, Ultimate | 6.20 MPa | 899 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 0.00900 GPa | 1.31 ksi | 1% Secant, ASTM D790 |
| Tensile Impact Strength | 502 kJ/m² | 239 ft-lb/in² | 23°C; ASTM D-1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 67.0 °C | 153 °F | Exxon Method |
| Vicat Softening Point | <= 23.0 °C | <= 73.4 °F | 1000g; ASTM D-1525 |