- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.926
- 拉伸强度 [MPa]: 10.0
- 弯曲强度 [MPa]: 19.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 48 | 48 | ASTM D2240 |
| Tensile Strength, Ultimate | 19.0 MPa | 2760 psi | ASTM D638 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM D638 |
| Film Elongation at Break, MD | 350 % | 350 % | ASTM D882 |
| Film Elongation at Break, TD | 500 % | 500 % | ASTM D882 |
| Elongation at Break | 650 % | 650 % | ASTM D638 |
| Modulus of Elasticity | 0.317 GPa | 46.0 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.166 GPa | 24.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.197 GPa | 28.6 ksi | ASTM D882 |
| Dart Drop | 6.69 g/micron | 170 g/mil | ASTM D1709 |
| Dart drop Test | 170 g | 0.375 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 28.0 MPa | 4060 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 96.0 °C | 205 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 5.5 % | 5.5 % | ASTM D1003 |
| Gloss | 65 % | 65 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 190 - 204 °C | 374 - 399 °F | |