- 密度 [g/cm3]: 0.95
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D1505 | ||
| Particle Size | >= 150 µm | >= 150 µm | pan, 7% | ||
| <= 1000 µm | <= 1000 µm | sieve < 5% | |||
| Vinyl Acetate Content | 28 % | 28 % | wt %; Exxon Mobil | ||
| Melt Index of Compound | 150 g/10 min @Load 2.16 kg, Temperature 190 °C | 150 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 3.30 MPa | 479 psi | ASTM D638 | ||
| Elongation at Break | 720 % | 720 % | 50 mm/min; ASTM D638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 68.0 °C | 154 °F | DSC; ASTM D3418 | ||
| 90.0 °C | 194 °F | fusing temperature | |||
| Descriptive Properties | |||||
| Max Dry Flow | max 33 sec/100g | ASTM | |||