- 熔体流动速率 [g/10min]: 0.75
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.940 g/cc | 0.940 g/cc | ISO 1183 |
| Vinyl Acetate Content | 17 % | 17 % | |
| Thickness | 40.0 microns | 1.57 mil | for samples tested on this data sheet |
| 25.0 - 300 microns | 0.984 - 11.8 mil | possible range, depending on extrusion conditions | |
| Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.75 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 6.30 MPa | 914 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 4.50 MPa | 653 psi | ISO 527-3 |
| Film Elongation at Break, MD | 320 % | 320 % | ISO 527-3 |
| Film Elongation at Break, TD | 660 % | 660 % | ISO 527-3 |
| Modulus of Elasticity | 0.0560 GPa | 8.12 ksi | ISO 527-2 |
| Elmendorf Tear Strength, MD | 1.80 g/micron | 45.7 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 4.10 g/micron | 104 g/mil | ISO 6383-2 |
| Dart drop Test | 680 g | 1.50 lb | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 38.0 MPa | 5510 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 39.0 MPa | 5660 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 89.0 °C | 192 °F | ISO 11357 |
| Vicat Softening Point | 69.0 °C | 156 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.0 % | 2.0 % | ISO 14782 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 - 180 °C | 302 - 356 °F | |