- 熔体流动速率 [g/10min]: 2.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.940 g/cc | 0.940 g/cc | ISO 1183 |
| Vinyl Acetate Content | 17.5 % | 17.5 % | |
| Thickness | 40.0 microns | 1.57 mil | for samples tested on this data sheet |
| 20.0 - 100 microns | 0.787 - 3.94 mil | possible range, depending on extrusion conditions | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 5.60 MPa | 812 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 4.60 MPa | 667 psi | ISO 527-3 |
| Film Elongation at Break, MD | 330 % | 330 % | ISO 527-3 |
| Film Elongation at Break, TD | 620 % | 620 % | ISO 527-3 |
| Modulus of Elasticity | 0.0500 GPa | 7.25 ksi | ISO 527-2 |
| Elmendorf Tear Strength, MD | 2.70 g/micron | 68.6 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 4.40 g/micron | 112 g/mil | ISO 6383-2 |
| Dart drop Test | 500 g | 1.10 lb | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 29.0 MPa | 4210 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 87.0 °C | 189 °F | ISO 11357 |
| Vicat Softening Point | 64.0 °C | 147 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.5 % | 1.5 % | ISO 14782 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 - 180 °C | 302 - 356 °F | |