- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.931
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.931 g/cc | 0.0336 lb/in³ | ASTM D1505 | ||
| Vinyl Acetate Content | 9.0 % | 9.0 % | |||
| Thickness | 31.8 microns | 1.25 mil | |||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 | ||
| Film Elongation at Break, TD | 950 % | 950 % | ASTM D882 | ||
| Dart Drop | 5.795 g/micron | 147.2 g/mil | ASTM D1709 | ||
| Dart drop Test | 184 g | 0.406 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 32.4 MPa | 4700 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 23.4 MPa | 3400 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 96.5 MPa | 14000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 124 MPa | 18000 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.8 % | 4.8 % | ASTM D1003 | ||
| Gloss | 60.5 % | 60.5 % | at 45º; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |||
| Descriptive Properties | |||||
| process | Film | ||||
| region | US & Canada | ||||