- 密度 [g/cm3]: 0.931
- 拉伸强度 [MPa]: 7.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.931 g/cc | 0.0336 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Tensile Modulus | 0.0650 GPa | 9.43 ksi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Dielectric Constant | 2.6 @Frequency 100 Hz | 2.6 @Frequency 100 Hz | |
| Dissipation Factor | 0.024 @Frequency 100 Hz | 0.024 @Frequency 100 Hz | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 160 µm/m-°C @Temperature 20.0 °C | 88.9 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 91.0 °C | 196 °F | |
| Flammability, UL94 | HB @Thickness 3.20 mm | HB @Thickness 0.126 in | |
| Oxygen Index | 19 % | 19 % | |